Special Anti-corrosion and coating HL—9058coating （HAILIN system）
Using scope of coating
1. Carbon-steel heat exchanger , carbon-steel water cooler, tube of re-boiler, air cooler or any other non-style heat-exchanger.
2.Working temperature is within 150℃，long-time working temperature is around 120℃.
Implementation standards
SH/T3540《producing and inspection rules for complicated coating of tube of steel heat-exchanger》
Suitable coating material
1.Freshwater,salt water, half-salt water, ocean water and industrial recycling water.
2.Acid medium and slightly alkaline medium.
3.Gasoline, diesel oil,solvent oil ,liquid hydrogen and benzene.
Technical property of coating
1.Coating ingredients : HL—9058anti-corrosion coating primer paint （Ⅰ）,top paint（Ⅱ）and solvent, the main composition of the coating is epoxy resin, silicon resin.
2.Coating solidification: resin may be solidified to membrane in the high temperature after coating. The coating is hard, flexible 40and clean, with good physical mechanical performance and chemical stable performance.
3.Anti-corrosion performance:：HL—9058coating is anti-acid, anti-weak alkali, water-resistance, salt-resistance, high-temperature resistance, anti-corrosion,anti-impact and anti-dirt.
Physical mechanical performance
|
项目
|
检测方法
|
HL-9058
|
|
底｜
|
面‖
|
|
颜 色
|
GB/T1722-92
|
浅土红色
|
铭绿色
|
|
附着力：（级）
|
GB/T1720-89
|
1
|
1
|
|
粘度涂—4杯S/25℃
|
GB/T1723-93
|
50
|
45
|
|
柔韧性：（mm）
|
GB/T1731-93
|
1
|
1
|
|
冲击强度Kg/cm2
|
GB/T1732-93
|
50
|
50
|
|
吸水率：%<0.4
|
HG/T2-1612-85
|
0.30
|
0.33
|
|
耐热性：（烘干后）℃
|
GB/T1735-89
|
150
|
150
|
|
硬 度
|
GB/T1730-93
|
>0.75
|
>0.76
|
|
耐湿性：（级）
|
GB/T1740-89
|
1
|
1
|
|
导热系数：（kcal/m.·℃·h）
|
|
0.75-1.34
|
0.75-1.34
|
|
固化方法℃
|
|
交联固化170
|
交联固化200
|
Anti-corrosion performance of coating
|
介质分类
|
介质名称
|
HL-9058
|
|
介质温度℃
|
浸泡时间
|
涂层状况
|
|
水
|
海水、咸水、纯水、工业循环水
|
沸腾
|
26个月
|
无变化
|
|
碱溶液
|
5%NH4OH、NaOH、KOH
|
沸腾
|
22个月
|
无变化
|
|
酸溶液
|
10%H2SO4、HCL、H3PO4
|
沸腾
|
22个月
|
无变化
|
|
有机溶剂
|
二甲苯、汽油、煤油、醛
|
常温
|
30个月
|
无变化
|
Not:1.Good thermal conductivity, good effect of anti-dirt, when measuring 150±30μm, the resistance is only 1.85×10-4㎡ .h.℃ .kcal, the heat-exchange efficiency will greatly improved when there is no high-resistant rust in the tube.
2.performance of heat-resistance :HL—9058 belongs to high-temperature resistant coating, the heat-resistant performance can use for a long time in the temperature around 100℃ ,sweeping temperature can not be above 150℃ /h.
3.Inspection index of coating quality.
A.Appearance inspection: clean in the surface, no foreign matters, no bubble, no fall, color and sense evaluation should be unanimous.
B.Thickness of coating: dry film thickness is150±30μm, follow the standard of SH/T3540.
C.Side-leakage of coating: testing by electrical spark, painting if there is leak point in the painting film.
D.Monitoring of painting film: mechanical collision or flexible friction should be avoided in the process of storage and transportation and disassembling repair before using and installation.
|